Temp Teeth Model Resin
Temp Teeth Model Resin is a type of 3D printing resin specifically designed for creating temporary dental models and prototypes. This resin is often used in dental laboratories and clinics to create accurate and detailed models of teeth and dental structures.
Highlights
【Teeth Textured Appearance】Temporary dental mold resin, the resin material for dentistry,is used for producing temporary teeth with a natural look and color of teeth. The mold can be used after treating on surface and polishing simply;The surface hardness is hiah so that the mold is more scratch resistance after secondary curing
【High precision】The attachments of Antinsky dental mold resin have good sharpness, can capture subtle features, and can fit tightly with the diaphragm.
【Low shrinkage】Specifically designed to reduce volume shrinkage, ensuring the dimensional stability of printed models.
【Excellent physical properties】The cured model has a smooth surface, excellent mechanical strength and hardness, with a hardness of 80~90D, and can be tapped and polished.
Technical Datasheet
Recommended Print Parameters
Recommended printing time: Bottom exposure time 20-30s, layer exposure time 3s- 4s. (6.6 inches monochrome LCD printer, light intensity 3500~4500µw/㎝²)
Bottom Lift Distance: 6mm
Lifting Distance: 6mm
Bottom Lift Speed: 60mm/min
Lifting Speed: 80mm/min
Retract Speed: 150mm/min
Wavelength: 385~410nm
Molding Test Environment and Standard:
①Temperature: 23±2℃
②Relative humidity: 50%RH±5%RH
③The standard of the test piece: ASTM
④Post curing condition: The test piece was placed in water under 405nm ultraviolet radiation of
200mw/cm² for one minute.
Technical Parameters after Mold
Technical Parameters after Molding:
1、Maximum force(KGF): 142.167±10%
2、Tensile strength(MPa): 33.514±10%
3、Deformation of maximum point of force(mm): 6.341±10%
4、Elongation at yield point(%): 6.3±10%
5、Elongation at break(%): 32.386±10%
6、Maximum bending strength(MPa): 36.196±10%
7、Flexural modulus(MPa): 970.14±10%
8、Hardness(Shore D)：76-82
9、Impact strength(j/m): 64.6±10%
10、Tensile modulus：430.646±10%